Smooth-On TASK™ 6

Article number: 751635466418
Availability: In stock (1)

TASK™ 6 low cost, high performance casting resin yields castings that are tan and virtually bubble free. This resin offers superior physical and performance properties compared to our popular Smooth-Cast™ Series of general purpose casting resins. Vacuum degassing is not necessary and it offers the convenience of a 1A:1B by volume or weight mix ratio.

TASK™ 6 has high tensile and flexural strength, as well as high flexural modulus. This plastic was formulated for a variety of industrial applications including pattern making and making prototype models. This resin is designed for casting in thicknesses up to ½” (1.27 cm).


Materials should be stored and used in a warm environment (73° F / 23° C). This product has a limited shelf life and should be used as soon as possible. All liquid urethanes are moisture sensitive and will absorb atmospheric moisture. Mixing tools and containers should be clean and made of metal, glass or plastic. Mixing should be done in a well-ventilated area. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.

Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.

Applying A Release Agent - A release agent is necessary to facilitate demolding when casting into or over most surfaces. Use a release agent made specifically for mold making (Universal™ Mold Release or Mann’s Ease Release™ 200 available from Smooth-On or your Smooth-On distributor). A liberal coat of release agent should be applied onto all surfaces that will contact the plastic.

IMPORTANT: To ensure thorough coverage, apply release and brush with a soft brush over all surfaces. Follow with a light mist coating and let the release agent dry for 30 minutes.

Smooth-On silicone rubber molds usually do not require a release agent unless casting silicone into the mold. Applying a release agent will prolong the life of the mold.

Measuring - The proper mixing ratio of TASK™ 6 is 1A:1B by weight or volume. Dispense the required amount of Part A into a mixing container. Measure out the appropriate amount of Part B and combine with Part A.

Mixing - Materials should be stored and used in a warm environment (73° F / 23° C). Shake or stir Part A & Part B before using. Add Part A to Part B and mix thoroughly. Stir slowly and deliberately making sure that you scrape the sides and bottom of the mixing container several times. Be careful not to splash low viscosity material out of container.

If tinting or pigmenting TASK™ 6, add the tint or pigment dispersion to Part B and mix thoroughly before adding Part. A.

IMPORTANT: Shelf life of product is reduced after opening. Remaining product should be used as soon as possible. Immediately replacing the lids on both containers after dispensing product will help prolong the shelf life of the unused product. XTEND-IT™ Dry Gas Blanket (available from Smooth-On) will significantly prolong the shelf life of unused liquid urethane products.

Pouring - If casting TASK™ 6 into a rubber mold, pour mixture in a single spot at the lowest point of the mold. If encapsulating an object, do not pour the mixture directly over the object. Let the mixture seek its level. A uniform flow will help minimize entrapped air. Pour mixture in a single spot at the lowest point of the mold. If encapsulating an object, do not pour the mixture directly over the object. Let the mixture seek its level. A uniform flow will help minimize entrapped air.

For Best Results . . . Best results are obtained using a pressure casting technique. After pouring the mixed compound, the entire casting assembly (mold, dam structure, etc.) is placed in a pressure chamber and subjected to 60 PSI (4.2 kg/cm2) air pressure for 16 hours.

Curing - Important: Use this product with at least room size ventilation or in proximity to a forced outlet air vent and do not inhale/breath fumes. Fumes, which may be visible with a significant mass concentration, will quickly dissipate with adequate ventilation. Castings with significant mass may be hot to the touch and irritate skin immediately following cure. Let casting cool to room temperature before handling.

Demold time of the finished casting depends on mass and mold configuration. Low mass or thin-walled castings will take longer to cure than castings with higher mass concentration.

If making rotational or hollow castings, backfilling with a rigid foam (Foam-iT! 5 or other) will provide lightweight reinforcement. Foam backfilling is recommended if castings will be subjected to temperatures above 85°F / 30°C.

Post Curing - Castings will reach “full cure” faster and achieve maximum physical properties and heat resistance if TASK™ 6 is post cured. Post curing is recommended if castings are thin or of low mass concentration. Castings should be post cured in a mold or support structure. Allow the material to cure for 6 - 8 hours at room temperature followed by 16 hours at 150 - 160°F (65 - 72°C). The casting or part should be allowed to cool to room temperature before handling.

If you are pouring less than 1/4 in. (0.64 cm) of material, the casting should be heat post cured. If desired thickness is greater than 3 in. (7.62 cm), it is recommended that consecutive casts be made (one pour on top of another) with 30 minutes in between each casting to allow for heat dissipation.

Performance - Cured castings of TASK™ 6 are rigid and durable. They resist moisture, moderate heat, solvents, dilute acids and can be machined, primed/painted or bonded to other surfaces (any release agent must be removed). Castings can be displayed outdoors after priming and painting.


Mix Ratio: 1A:1B by weight or volume
Mixed Viscosity (ASTM D-2393): 800
Specific Gravity (ASTM D-1475): g/cc; 1.07
Specific Volume (ASTM D-1475): cu. in./lb.; 25.9
Pot Life @ 73° F / 23°C (ASTM D-2471): 7 Minutes
Demold Time**: 75 Minutes **Mass Dependent
Cure Time: 24 Hours
Color: Tan
Shore D Hardness (ASTM D-2240): 75
Ultimate Tensile (ASTM D-638): 5,200 psi
Tensile Modulus (ASTM D-638): 146,000 psi
Elongation at Break % (ASTM D-638): 4%
Flexural Strength (ASTM D-790): 6,200 psi
Flexural Modulus (ASTM D-790): 182,500 psi
Compressive Strength (ASTM D-695): 5,570 psi
Heat Deflection Temp (ASTM D-648): 162°F/72°C
Compressive Modulus (ASTM D-695): 65,000 psi
Shrinkage in./in. (ASTM D-2566): 0.0031
All values measured after 7 days at 73°F/23°C: